In-house laboratory test report for Epoxy Polyester Glossy on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Gloss 88–90 GU at 60°, salt spray 500–750 hrs (ASTM B117), humidity 800–1000 hrs, cross-hatch adhesion 5B, impact ≥100 kg·cm². Report OI/QC/PC/2026-0147.
Download PDFIn-house laboratory test report for Epoxy Polyester Matt on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Gloss 8–10 GU at 60°, salt spray 500–750 hrs (ASTM B117), humidity 800–1000 hrs, cross-hatch adhesion 5B, impact ≥100 kg·cm². Report OI/QC/PC/2026-0148.
Download PDFIn-house laboratory test report for Epoxy Polyester Satin on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Gloss 55–60 GU at 60°, film thickness 70–80 µm, salt spray 500–750 hrs (ASTM B117), humidity 800–1000 hrs, adhesion 5B, impact ≥100 kg·cm². Report OI/QC/PC/2026-0149.
Download PDFIn-house laboratory test report for Polyurethane powder coating (matt, satin and gloss) on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Cure 180–200 °C metal temperature for 10–15 min, film 70–80 µm, salt spray ≥1200 hrs (ASTM B117), humidity ≥1500 hrs, adhesion 5B, impact ≥120 kg·cm. Report OI/QC/PU/2026-0150.
Download PDFIn-house laboratory test report for Pure Epoxy Dead Matt on 0.8 mm aluminium with 7-stage zinc phosphate pre-treatment. Cure 200 °C metal temperature for 10–15 min, film 75–80 µm, gloss 5–8 GU at 60°, salt spray 1000–1300 hrs (ASTM B117), humidity 800–1000 hrs, adhesion 5B, impact ≥120 kg·cm². Report OI/QC/EP/2026-0151.
Download PDFIn-house laboratory test report for Pure Polyester Glossy on 0.8 mm aluminium with 5-stage zinc phosphate pre-treatment. Cure 180–200 °C metal temperature for 10–15 min, film 75–80 µm, gloss 90–93 GU at 60°, salt spray 500–750 hrs (ASTM B117), humidity ≥1000 hrs, QUV 700–1000 hrs (ASTM G154), adhesion 5B, impact ≥110 kg·cm². Report OI/QC/PP/2026-0152.
Download PDFIn-house laboratory test report for Pure Polyester Matt on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Cure 180–200 °C metal temperature for 10–15 min, film 75–80 µm, gloss 9–11 GU at 60°, salt spray 500–750 hrs (ASTM B117), humidity ≥1000 hrs, QUV 700–1000 hrs (ASTM G154), adhesion 5B, impact ≥110 kg·cm². Report OI/QC/PP/2026-0153.
Download PDFIn-house laboratory test report for Pure Polyester Satin on 0.8 mm mild steel with 5-stage zinc phosphate pre-treatment. Cure 180–200 °C metal temperature for 10–15 min, film 75–80 µm, gloss 60–70 GU at 60°, salt spray 500–750 hrs (ASTM B117), humidity ≥1000 hrs, QUV 700–1000 hrs (ASTM G154), adhesion 5B, impact ≥110 kg·cm². Report OI/QC/PP/2026-0154.